Method for forming an integrated circuit interconnect using a dual poly process

ABSTRACT

A method for forming an electrical interconnect overlying a buried contact region of a substrate is characterized by a deposition of a first polycrystalline silicon layer and the patterning and etching of same to form a via. The via is formed in the first polycrystalline silicon layer to expose the substrate and a second polycrystalline silicon layer is formed in the via to contact the substrate. Portions of the second polycrystalline silicon layer overlying the first polycrystalline silicon layer are removed eliminating any horizontal interface between the two polycrystalline silicon layers. The first polycrystalline silicon layer remaining after the etch is then patterned to form an electrical interconnect.

FIELD OF THE INVENTION

[0001] The invention is related to fabrication of a semiconductor, and more particularly to the fabrication of a polycrystalline silicon interconnect.

BACKGROUND ART

[0002] In some semiconductor buried contact applications upper 1 and lower 2 polycrystalline silicon layers form an electrical interconnect 3 to a substrate, see FIG. 1A. In the process for forming the electrical interconnect 3 polycrystalline silicon layer 1 is masked to define the electrical interconnect 3. Polysilicon 1, overlying polycrystalline silicon 2, and polycrystalline silicon 2 are etched to form the interconnect according to the mask. Typically a defect can occur along the horizontal interface between the upper 1 and lower 2 polycrystalline silicon layers. In one case the defect degrades the integrity of the electrical contact by preventing etching of the lower polycrystalline silicon layer in areas which are exposed during etching. This polycrystalline silicon which is not etched when intended can bridge between two poly interconnects thereby causing malfinctions in the part.

[0003] In one solution a single poly process is used, see Figure lB. In the single poly process a single layer of polycrystalline silicon is deposited and masked to form an electrical interconnect 4. However contamination problems occur at the poly/oxide interface during buried contact formation when the single poly process is used. In addition a required hydro-fluoric acid etch thins the gate oxide layer creating a non uniform gate oxide.

[0004] In addition when patterning a polycrystalline silicon above a buried contact region, trenching of the substrate and exposure of the buried contact region often occur due to misalignment. Thus a need exists to protect the buried contact from exposure and trenching during gate patterning. In one solution a buried contact cap is used to protect the buried contact region. However a parasitic transistor is formed around the contact cap thereby degrading the performance of the device. In one solution an implant mask has been added to lower contact resistance and eliminate parasitic transistor problems.

[0005] Thus a need exits for a method having minimal contamination when forming a polycrystalline silicon interconnect which has integrity within the contact without reflective notching. The method must also retain a conformal gate oxide layer without trenching or exposing the substrate.

SUMMARY OF THE INVNTION

[0006] The invention is a method for forming an electrical interconnect, typically of polycrystalline silicon (although amorphous silicon or other electrically conductive materials may be used), overlying a buried contact region of a substrate. A first electrically conductive layer, typically of polycrystalline silicon (poly 1), is deposited to overlie the substrate. The poly 1 is patterned and etched to form a via thereby exposing the substrate. A second electrically conductive layer, typically of polycrystalline silicon (poly 2), is deposited to overlie the substrate and the poly 1 layer. In a first embodiment the poly 2 layer is chemically mechanically planarized to remove the poly 2 layer overlying the poly 1 layer thereby eliminating a horizontal interface between the poly 1 and the poly 2 layers.

[0007] In a second embodiment a layer resistant to a polycrystalline silicon etch is created prior to the patterning and etch of the poly 1 layer and prior to the deposition of the poly 2 layer. This layer will be referred to as a first polycrystalline silicon etch stop layer or just first etch stop layer. The first etch stop layer is patterned and etched to expose the poly 1 in the buried contact region. The poly 1 layer is then etched to expose the buried contact region of the substrate and poly 2 is deposited to overlie the remaining first etch stop layer and buried contact region. The poly 2 is then removed to expose the etch stop layer. Poly 2 remains in the via.

[0008] At this juncture a layer which is capable of reacting with silicon to form a silicon etch stop layer is deposited to overlie the first etch stop layer and the second polycrystalline silicon layer. A reaction is created between the second polycrystalline silicon layer and the layer which is capable of reacting with silicon, typically titanium. A second etch stop layer, resistant to a polycrystalline silicon etch, is formed overlying the poly 2 layer as a result of the reaction. The first etch stop layer functions as a protective layer during the reaction to prohibit a reaction between the poly 1 layer and the layer which is capable of reacting with silicon. The second etch stop layer eliminates trenching and exposure of the substrate even with gross misalignment of the photoresist mask during an etch of the poly 1 to form the interconnect.

[0009] In a further embodiment the invention is a semiconductor interconnect for electrically connecting a first region of a substrate and a second region of the substrate. The semiconductor interconnect comprises an electrically conductive silicon plug overlying and in electrical contact with the first region and the second region and an electrically conductive silicon layer, without a silicon interface horizontal to the substrate. The electrically conductive silicon layer is electrically isolated from the substrate and interposed between the silicon plug overlying the first region and the silicon plug overlying the second region. The interface between the silicon plug overlying the first region and the silicon layer is vertical to the substrate as is the interface between the silicon plug overlying the second region and the silicon layer.

BRIEF DESCRIPTION OF THE DRAWINGS

[0010]FIGS. 1A and 1B are cross-sectional views of electrical interconnects of the related art.

[0011] FIGS. 2-12 depict the steps of the invention in cross section.

[0012] In FIG. 2A a first polycrystalline silicon layer has been deposited to overlie a substrate and has been patterned to define a buried contact region.

[0013] In FIG. 2B a first polycrystalline silicon layer and an etch stop layer have been deposited to overlie a substrate and have been patterned to define a buried contact region.

[0014] In FIGS. 3A and 3B the substrate has been exposed.

[0015] In FIGS. 4A and 4B a second polycrystalline silicon layer has been deposited.

[0016] In FIGS. 5A and 5B the second polycrystalline silicon layer has been removed in areas overlying the first polycrystalline silicon layer.

[0017] In FIGS. 6A and 6B a gate region has been patterned.

[0018] In FIGS. 7A and 7B the first polycrystalline silicon layer has been etched to form the gate region.

[0019] In FIG. 8 a titanium layer has been deposited to overlie the etch stop layer and second polycrystalline silicon layer of Figure 5B.

[0020] In FIG. 9 an etch stop layer is formed overlying the second polycrystalline silicon layer and the titanium is removed.

[0021] In FIG. 10 the etch stop layer of FIG. 2B is removed.

[0022] In FIG. 11 a gate region is patterned and the first polycrystalline silicon layer is removed in unmasked regions.

[0023] In FIG. 12 the pattern has been removed.

DETAILED DESCRIPTION OF THE INVENTION

[0024] The invention is a method for forming an electrical interconnect of polycrystalline silicon overlying a buried contact region of a substrate. The method is depicted in cross section in FIGS. 2-12.

[0025] In the embodiments shown in FIGS. 2A and 2B field oxide regions 5 and a gate oxide layer 10 are formed by conventional methods to overlie a substrate 15. A first polycrystalline silicon layer 20 (poly 1) is deposited to overlie the field oxide regions 5 and gate oxide 10. The thickness of the first polycrystalline silicon layer 20 is selected such that the lowest upper surface of the first polycrystalline silicon layer 20 is higher than the highest upper surface of the field oxide regions 5. The polycrystalline silicon layer 20 is then patterned with photoresist mask 25.

[0026] In the second embodiment, shown in FIG. 2B, a polycrystalline silicon etch stop layer 30, also referred to as just etch stop layer 30, is deposited to overlie the first polycrystalline silicon layer 20 prior to patterning with photoresist mask 25. The etch stop layer is irresponsive to a polycrystalline silicon etch. In this embodiment the etch stop layer is oxide although nitride or some other material may also be used.

[0027] Next the first polycrystalline silicon layer 20 and the gate oxide layer 10 are etched by conventional methods in unmasked region 35 to exposed the buried contact portion 40 oflthe substrate 15, thereby forming a via 41. This is shown in FIGS. 3A and 3B for the first and the second embodiments respectively. In the second embodiment, see FIG. 3B, a separate etch is conducted prior to the polycrystalline silicon etch to remove the etch stop layer 30 in the unmasked region 35. Subsequent to the formation of via 41 the photoresist mask 25 are removed.

[0028] In FIGS. 4A and 4B of the first and second embodiments a second polycrystalline silicon layer 45 (poly 2) is deposited to overlie the first polycrystalline silicon layer 20 and the buried contact portion 40. In the second embodiment the second polycrystalline silicon layer 45 also overlies the etch stop layer 30 and must be thick enough to fill the via 41.

[0029] In the first embodiment, see FIG. 5A, a chemical mechanical planarization removes the second polycrystalline silicon 45 overlying the first polycrystalline silicon layer 20 to expose the first polycrystalline silicon layer 20 thereby eliminating a poly I and poly 2 horizontal interface. It can be seen that the height of the first polycrystalline layer 20 defines the height of the second polycrystalline silicon layer 45 after the planarization. There may be some loss of the original height of the firt polycrystalline layer 20 due to a loss during the chemical mechanical planarization, but it is typically negligible.

[0030] In the second embodiment, see Figure SB a polycrystalline silicon etch is used to remove the poly 2 layer 45 overlying the poly I layer 20 and etch stop layer 30. In this case it can be seen that the total height of the poly 1 layer 20 and the etch stop layer 30 defines the maximum height of the poly 2 layer 45 after the etch. However, the etch typically consumes additional portions of poly 2 layer 45 such that the upper portion of the poly 2 layer 45 is below the surface of the etch stop layer 30. After removal of the poly 2 layer 45 overlying the poly 1 layer 20 the second polycrystalline silicon layer 45 remaining in via 41 forms a contact plug in electrical contact withy buried contact portion 40.

[0031] In all of the embodiments the first and second polycrystalline silicon layers are doped to increase conductivity. The preferred doping comprises implanting arsenic and then performing an anneal to diff-use the arsenic. A doped region 46 is created in the buried contact portion 40 of the substrate by diffusion or other means. The doped region 46 typically contacts other difflusion regions in the substrate which are not shown in the present figures but which are well known to those skilled in the art. The exact point or points in the process where doping is performed is subject to manufacturing considerations and is therefore determined at the time of manufacture by a person skilled in the art.

[0032] At this junction the method may proceed along two alternate paths to form the contact plug of the invention. FIGS. 6 and 7 represent the first path and FIGS. 8-12 represent the second path.

[0033] In FIGS. 6A and 6B the first polycrystalline silicon layer 20 is patterned with a photoresist mask 50 to define an electrical interconnect comprising the contact plug of polycrystalline silicon layer 45 and the first polycrystalline silicon layer 20. The electrical interconnect may have different functions and is patterned according to the finction desired. In addition to providing electrical access to the buried contact portion 40 the contact plug may form a gate for a field effect transistor or may provide electrical contact to further circuit components. If the photoresist mask 50 is designed to overlap the upper surface of the second poly 2 layer 45 the trenching and exposure of the substrate is eliminated during the etch of the poly 1 layer 20. An optional oxide layer may be deposited to overlie the poly 1 and poly 2 layers 20 and 45 prior to the masking.

[0034] The poly 2 layer 20, and the optional oxide layer when deposited, in FIG. 6A and etch stop layer 30 in FIG. 6B are then etched in exposed areas. The photoresist mask 50 is then removed to form the electrical interconnect 55 comprising the contact plug and polycrystalline silicon layer 20 as shown in FIGS. 7A and 7B for the first and second embodiments, respectively.

[0035] In the second path a titanium layer 60 is deposited to overlie the etch stop layer 30 and the poly 2 layer 45 of FIG. 6B, see FIG. 8.

[0036] Next the structure is heated to a temperature conducive to forming titanium silicide. The poly 2 layer 45 reacts with the titanium during heating to form titanium silicide which functions as a silicon etch stop layer 65, see FIG. 9. The nonreacted titanium 60 overlying the etch stop layer 30 is removed following the formation of the titanium silicide 65, also see FIG. 9. The etch stop layer 30 functions as a protective layer prohibiting a reaction between the titanium layer 60 and the poly I layer 20 during the reaction of the poly 2 layer 45 with the titanium layer 60.

[0037] Optionally, in place of a titanium deposit 60 and subsequent formation of etch stop layer 65 of titanium silicide, oxide may be grown overlying poly 2 layer 45 during an anneal. The result is similar to the structure shown in FIG. 9. However in this case the etch stop layer 30 is nitride and the etch stop layer 65 is oxide.

[0038] In either case, the etch stop layer 30 may be removed subsequent to the formation of etch stop layer 65, see FIG. 10.

[0039] The electrical interconnect is patterned with photoresist mask 70 in FIG. 11. The poly 1 layer 20, and etch stop layer 30 if not already removed, is removed in exposed regions. Since silicon is selectively etchable over the etch stop layer 65 trenching and exposure of the substrate are eliminated during the etch of the poly 1 layer 20 due to the protection afforded the substrate by the etch stop layer 65, either titanium silicide or oxide, during the etch. The etch stop layer 65 is used during the formation of the electrical interconnect 80 to protect the second polycrystalline silicon 45 during the formation of the electrical interconnect 80. The polycrystalline silicon etch is highly selective over titanium silicide or oxide. By using this path of the second embodiment it is possible to eliminate trenching and exposure of the substrate even with gross misalignment of the photoresist mask.

[0040] The electrical interconnect 80 and contact plug formed from poly 2 layer 45 are shown following the removal of the photoresist mask 70. Since it was not necessary to use a contact cap to form the interconnect 80 parasitic transistor formation is eliminated. In addition cell size is reduced over methods using a contact cap.

[0041] The electrical interconnect formed by the method of the invention may be used in the manufacture of static random access memories (SRAMs) as well as dynamic random access memories.

[0042] Although the present invention has been described with reference to particular embodiments, other versions are possible and will be apparent to individuals skilled in the art; The invention therefore, is not limited to the specific features and elements shown. It is intended that the scope of the invention be defined by the appended claims and in accordance with the doctrine of equivalents. 

What is claimed is:
 1. A method for forming an electrical interconnect, comprising the following steps: a) creating a first electrically conductive layer overlying a substrate and having an opening therein exposing a portion of the substrate; b) creating a second electrically conductive layer to overlie said first electrically conductive layer and the substrate, said second electrically conductive layer electrically contacting the substrate in the portion of the substrate which was exposed; and c) removing said second electrically conductive layer from overlying said first electrically conductive layer, a portion of said second electrically conductive layer remaining in electrical contact with the portion of the substrate which was exposed.
 2. A method for forming an electrical interconnect, comprising the following steps: a) creating a first electrically conductive layer overlying a substrate; b) patterning said first electrically conductive layer to create a masked region and an unmasked region; c) exposing the substrate in said unmasked region, thereby forming a via in said first electrically conductive layer, d) creating a second electrically conductive layer to overlie said first electrically conductive layer and the substrate, said second electrically conductive layer electrically contacting the substrate in the unmasked region; and e) removing said second electrically conductive layer from overlying said first electrically conductive layer, a portion of said second electrically conductive layer remaining in the via and contacting the substrate to form the electrical interconnect.
 3. A method for forming an electrical interconnect, comprising the following steps: a) creating b first electrically conductive layer overlying a substrate; b) patterning said first electrically conductive layer to create a masked region and an unmasked region; c) exposing the substrate in said unmasked region, thereby forming a via in said first electrically conductive layer; d) creating a second electrically conductive layer to overlie said first electrically conductive layer and the substrate, said second electrically conductive layer electrically contacting the substrate in the unmasked region; e) removing said second electrically conductive layer from overlying said first electrically conductive layer, a portion of said second electrically conductive layer remaining in the via and contacting the substrate to an electrical plug, the electrical plug and the first electrically conductive layer forming the electrical interconnect; and f) retaining a portion of said first electrically conductive layer during said step of removing.
 4. The method as specified in claim 3 , defining a height of the electrical plug by a height of said first electrically conductive layer remaining subsequent to said step of removing, such that the height of the electrical plug is equal to the height of said first electrically conductive layer.
 5. The method as specified in claim 3 , further comprising the following steps: a) creating an etch stop layer overlying said first electrically conductive layer prior to said step of exposing, the via thereby formed in said first electrically conductive layer and said etch stop layer; and b) defining a maximum height of the electrical plug by a total height of said first electrically conductive layer and said etch stop layer, such that the height of the electrical plug is equal to or less than the total height of said first electrically conductive layer and said etch stop layer.
 6. The method as specified in claim 5 , wherein said step of exposing comprises etching said first electrically conductive layer and said etch stop layer.
 7. The method as specified in claim 5 , wherein said step of removing comprises etching said second electrically conductive layer, said etch stop layer protecting said first electrically conductive layer during said step of removing.
 8. The method as specified in claim 3 , wherein said step of removing comprises performing a chemical mechanical planarization of said second electrically conductive layer to expose said first electrically conductive layer.
 9. The method as specified in claim 3 , wherein said step of removing comprisesetching said second electrically conductive layer.
 10. The method as specified in claim 3 , further comprising the following steps: a) protecting at least said second electrically conductive layer with a photoresist mask; and b) removing exposed portions of said first electrically conductive layer, remaining portions of said first electrically conductive layer vertically and electrically contacting the electrical plug.
 11. The method as specified in claim 10 , further comprising the step of creating a protective layer overlying said second electrically conductive layer remaining subsequent to said step of removing said second electrically conductive layer, said protective layer protecting said second electrically conductive layer during said step of removing exposed portions of said first electrically conductive layer.
 12. The method as specified in claim 3 , further comprising the following steps: a) creating a first etch stop layer overlying said first electrically conductive layer prior to said step of exposing; b) creating a layer which is capable of reacting with said second electrically conductive layer to form a layer irresponsive to an etchant which is capable of etching said second electrically conductive layer, said layer which is capable of reacting with said second electrically conductive layer overlying said first etch stop layer and said the electrical plug; c) creating a reaction between said layer which is capable of reacting with said second electrically conductive layer and the electrical plug to form a second etch stop layer overlying the electrical plug, said first etch stop layer protecting said first electrically conductive layer from reacting with said layer which is capable of reacting with said second electrically conductive layer during said step of creating said reaction; d) removing unreacted portions of said layer which is capable of reacting with said second electrically conductive layer; e) removing at least portions of said first etch stop layer while retaining said second etch stop layer, f) removing at least portions of said first electrically. conductive layer to further define a shape of the electrical interconnect; and g) retaining the electrical plug in its entirety during said steps (e and f of claim 12 ) of removing.
 13. The method as specified in claim 3 , further comprising doping said first and said second electrically conductive layers to increase a conductivity thereof.
 14. The method as specified in claim 3 , further comprising the step of using silicon as said first and said second electrically conductive layers.
 15. A method for forming an electrical interconnect, comprising the following steps: a) creating a first electrically conductive layer overlying a substrate; b) patterning said first electrically conductive layer to create a masked region and an unmasked region; c) exposing the substrate in said unmasked region; d) creating a second electrically conductive layer to overlie said first electrically conductive layer and the substrate, said second electrically conductive layer contacting the substrate in the urunasked region; and e) chemical mechanical planarizing of a portion of said second electrically conductive layer to expose said first electrically conductive layer, a further portion of said second electrically conductive layer remaining in contact with the substrate.
 16. The method as specified in claim 15 , further comprising the step of using silicon as said first and said second electrically conductive layers.
 17. A method for forming an electrical interconnect, comprising the following steps: a) creating a first electrically conductive layer overlying a substrate; b) creating an etch stop layer overlying said first electrically conductive layer; c) patterning said first electrically conductive layer and said etch stop layer to create a masked region and an unmasked region; d) exposing the substrate in said unmasked region, thereby forming a via having a sidewall comprising said first electrically conductive layer and said etch stop layer; e) creating a second electrically conductive layer to overlie said etch stop layer and the substrate, said second electrically conductive layer electrically contacting the substrate in the unmasked region; and f) etching a portion of said second electrically conductive layer to expose said etch stop layer, at least a portion of said second electrically conductive layer remaining in electrical contact with the substrate to form a electrical plug of the electrical interconnect.
 18. The method as specified in claim 17 , wherein the etch stop layer is a first etch stop layer and further comprising the following steps: a) creating, overlying said first etch stop layer and the electrical contact, a layer which is capable of reacting with said second electrically conductive layer to form a layer which is irresponsive to an etchant which is capable of etching said second electrically conductive layer; b) creating a reaction between said layer which is capable of reacting with said second electrically conductive layer and the electrical contact to form a second etch stop layer overlying the electrical contact, said first etch stop layer protecting said first electrically conductive layer from reacting with said layer which is capable of reacting with said second electrically conductive layer during said step of creating said reaction; c) removing unreacted portions of said layer which is capable of reacting with said second electrically conductive layer; d) removing at least portions of said first etch stop layer while retaining said second etch stop layer; e) removing at least portions of said first electrically conductive layer, while retaining the electrical plug in its entirety during said steps (d and e) of removing to form the electrical interconnect of the electrical plug and the remaining portion of the first electrically conductive layer.
 19. The method as specified in claim 17 , further comprising the step of forming a protective layer overlying the electrical contact, said protective layer protecting the electrical contact during subsequent etching of said first electrically conductive layer.
 20. The method as specified in claim 17 , flirter comprising the following steps: a) depositing a titanium layer overlying said etch stop layer and the electrical contact; and b) forming a layer of titanium silicide overlying the electrical contact.
 21. The method as specified in claim 20 , further comprising the following steps: a) removing at least portions of said first electrically conductive layer; and b) retaining the electrical plug in its entirety during said step of removing.
 22. The method as specified in claim 17 , further comprising the step of forming an oxide layer overlying the electrical contact.
 23. The method as specified in claim 22 , further comprising the following steps: a) removing at least portions of said first electrically conductive layer, and b) retaining the electrical plug underlying said oxide layer during said step of removing.
 24. The method as specified in claim 17 , wherein said step of exposing comprises the following steps: a) etching said etch stop layer, and b) etching the first electrically conductive layer.
 25. The method as specified in claim 17 , firther comprising using silicon as said first and said second electrically conductive layers.
 26. A method for forming an electrical interconnect to a substrate, comprising the following steps: a) depositing a first electrically conductive layer to overlie a substrate; b) etching said first electrically conductive layer to form a via and expose a portion of the substrate at a bottom of the via; c) depositing a second electrically conductive layer in said via to electrically contact the substrate and to overlie said first electrically conductive layer; and d) removing said second electrically conductive layer overlying said first electrically conductive layer thereby eliminating a horizontal interface between saidfirst and said second electrically conductive layers while retaining a portion of said second electrically conductive contacting the substrate.
 27. The method as specified in claim 26 , further comprising using silicon as said first and said second electrically conductive layers.
 28. A semiconductor interconnect for electrically connecting a first region of a substrate and a second region of the substrate, comprising: a) an electrically conductive silicon plug overlying and in electrical contact with the first region and the second region; and b) an electrically conductive silicon layer, without a silicon interface horizontal to the substrate, electrically isolated from the substrate and interposed between said silicon plug overlying the first region and said silicon plug overlying the second region, wherein an interface between said silicon plug overlying the first region and said silicon layer is vertical to the substrate, and wherein an interface between said silicon plug overlying the second region and said silicon layer is vertical to the substrate.
 29. A static random access memory device having an electrical interconnect for electrically connecting a first region of a substrate and a second region of the substrate, comprising: a) an electrically conductive silicon plug overlying and in electrical contact with the first region and the second region; and b) an electrically conductive silicon layer, without a silicon interface horizontal to the substrate, electrically isolated from the substrate and interposed between said silicon plug overlying the first region and said silicon plug overlying the second region, wherein an interface between said silicon plug overlying the first region and said silicon layer is vertical to the substrate, and wherein an interface between said silicon plug overlying the second region and said silicon layer is vertical to the substrate.
 30. A dynamic random access memory device having an electrical interconnect for electrically connecting a first region of a substrate and a second region of the substrate, comprising: a) an electrically conductive silicon plug overlying and in electrical contact with the first region and the second region; and b) an electrically conductive silicon layer, without a silicon interface horizontal to the substrate, electrically isolated from the substrate and interposed between said silicon plug overlying the first region and said silicon plug overlying the second region, wherein an interface between said silicon plug overlying the first region and said silicon layer is vertical to the substrate, and wherein an interface between said silicon plug overlying the second region and said silicon layer is vertical to the substrate.
 31. An electrical interconnect formed by the process, comprising the following steps: a) creating a first electrically conductive layer overlying a substrate and having an opening therein exposing a portion of the substrate; b) creating a second electrically conductive layer to overlie said first electrically conductive layer and the substrate, said second electrically conductive layer electrically contacting the substrate in the portion of the substrate which was exposed; and c) removing said second electrically conductive layer from overlying said first electrically conductive layer, a portion of said second electrically conductive layer remaining in electrical contact with the portion of the substrate which was exposed.
 32. A static random access memory device made by the process, comprising the following steps: a) creating a first electrically conductive layer overlying a substrate and having an opening therein exposing a portion of the substrate; b) creating a second electrically conductive layer to overlie said first electrically conductive layer and the substrate, said second electrically conductive layer electrically contacting the substrate in the portion of the substrate which was exposed; and c) removing said second electrically conductive layer from overlying said first electrically conductive layer, a portion of said second electrically conductive layer remaining in electrical contact with the portion of the substrate which was exposed.
 33. A dynamic random access memory formed by the process comprising, comprising the following steps: a) creating a first electrically conductive layer overlying a substrate and having an opening therein exposing a portion of the substrate; b) creating a second electrically conductive layer to overlie said first electrically conductive layer and the substrate, said second electrically conductive layer electrically contacting the substrate in the portion of the substrate which was exposed; and c) removing said second electrically conductive layer from overlying said first electrically conductive layer, a portion of said second electrically conductive layer remaining in electrical contact with the portion of the substrate which was exposed. 